DeWAL D/W 200
聚四氟乙烯
DeWAL Industries

产品说明

D/W 200 is skived from a modified homopolymer PTFE resin containing a higher level of a fully fluorinated comonomer than is in our 220 film. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally bonded (fused) to itself (625 - 650 degrees F). The modified homopolymer resin exhibits chemical resistance equivalent to that of homopolymer PTFE. Its tensile strength is approximately 25% higher, and the elongation is approximately 60% higher than for homopolymer PTFE. Because of these properties D/W 200 is often a good substitute for melt Processable films such as PFA.

D/W 200 may be thermally fused to itself making possible the fabrication of structures requiring these properties. D/W 200 can also be used as a high dielectric strength fusible wrap in electrical and electronic cable applications. It can also be used as a bonding film in the circuit board industry.

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 欧洲  
性能特点 • 均聚物 • 良好的电气性能 • 耐化学性良好 
用途 • 薄膜 • 电子电缆护套材料  
 • 电气/电子应用领域 • 粘合  
    
形式 • 薄膜   

物理性能 额定值单位制 
Thickness 12.7 到 1570nm 
薄膜 额定值单位制 测试方法
抗张强度 - MD (屈服) 41.4MPa ASTM D882
伸长率 - MD (断裂) 500% ASTM D882
热性能 额定值单位制 
最高连续使用温度 260°C 
电气性能 额定值单位制 测试方法
介电强度 110kV/mm ASTM D149
补充信息 额定值单位制 
Backing Material PTFE Film 
Core ID 7.62cm 
Maximum Roll OD 356mm 
Width 25.4 到 914mm 

备注
1 一般属性：这些不能被视为规格。